PRIMACOR™ 5990I
Copolymer
The Dow Chemical Company
产品说明:
-
Low heat seal temperature, high hot tack
-
High gloss, excellent clarity
-
Excellent water, grease and oil resistance
Complies with
-
U.S. FDA 21 CFR 177.1310(a)(2)
PRIMACOR™ 5990I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. In dispersion form, it is a versatile binder for nonwoven fibers, including polypropylene, polyester, glass, nylon and others.
Applications:
Outstanding Properties:
-
Dispersible in aqueous amines and alkali
-
"Clean" dispersion requires no salts, surfactants or solvents
-
Dispersions use existing waterbourne application equipment
PRIMACOR™ 5990I 物性表
基本信息
|
|
机构评级
|
-
FDA 21 CFR 177.1310 (a) 2
|
形式
|
|
加工方法
|
|
物理性能
|
额定值
|
单位制
|
测试方法
|
比重
|
0.955
|
g/cm3
|
ASTM D792, ISO 1183
|
熔流率(熔体流动速率)
|
|
|
ASTM D1238, ISO 1133
|
125°C/2.16 kg 1
|
65
|
g/10 min
|
ASTM D1238, ISO 1133
|
190°C/2.16 kg 2
|
1300
|
g/10 min
|
ASTM D1238, ISO 1133
|
共聚单体含量 3
|
20.0
|
%
|
内部方法
|
机械性能
|
额定值
|
单位制
|
测试方法
|
拉伸模量 - 2% 正割 (模压成型)
|
22.1
|
MPa
|
ASTM D638, ISO 527-2
|
抗张强度 (断裂, 模压成型)
|
6.21
|
MPa
|
ASTM D638, ISO 527-2
|
伸长率 (断裂, 模压成型)
|
350
|
%
|
ASTM D638, ISO 527-2
|
热性能
|
额定值
|
单位制
|
测试方法
|
维卡软化温度
|
40.0
|
°C
|
ASTM D1525, ISO 306
|
溶融温度(DSC)
|
75.0
|
°C
|
内部方法
|
挤压说明
|
用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。
|
备注
|
1 .
|
如同在生产时测量的一样。
|
2 .
|
熔体指数值和熔体流动速率相关联(ASTM D 1238 条件为 125°C/2.16kg)。
|
3 .
|
通过 Dow 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的
|
...