Nilit Nilamid A3 H G10 50% Glass Reinforced PA66

Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 50% Glass Fiber Filled

Nilit

产品说明:

Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance, even at elevated temperatures. It is used for highly loaded applications like high torque transmission housings, electrical cable holders and tensioners of ski bindings.

Key characteristics:

• High stiffness
• High strength
• Good impact strength
• Excellent thermal performance
• Good creep resistance

Information provided by NILIT.

Nilit Nilamid A3 H G10 50% Glass Reinforced PA66 物性表

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.57 g/cc	0.0567 lb/in3	ASTM D792, ISO 1183
吸水率	0.50 %	0.50 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
饱和吸水率	3.5 %	3.5 %	sim. ISO 62
线性成型收缩率,Flow	0.0020 cm/cm	0.0020 in/in	Euronil
线性成型收缩率，横向	0.0030 cm/cm	0.0030 in/in	Euronil

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(屈服)	220 MPa	31900 psi	ISO 527, ASTM D638
伸长率 (断裂)	2.0 %	2.0 %	ISO 527, ASTM D638
拉伸模量	16.5 GPa	2390 ksi	ISO 527, ASTM D638
弯曲强度	310 MPa	45000 psi	ISO 178, ASTM D790
	230 MPa @Temperature 90.0 °C	33400 psi @Temperature 194 °F	ISO 178, ASTM D790
弯曲模量	15.0 GPa	2180 ksi	ISO 178, ASTM D790
	9.50 GPa @Temperature 90.0 °C	1380 ksi @Temperature 194 °F	ISO 178, ASTM D790
悬壁梁缺口冲击强度	13.0 kJ/m2 @Temperature -30.0 °C	6.19 ft-lb/in2 @Temperature -22.0 °F	ISO 180/1A
	16.0 kJ/m2 @Temperature 23.0 °C	7.61 ft-lb/in2 @Temperature 73.4 °F	ISO 180/1A
简支梁无缺口冲击强度	7.00 J/cm2	33.3 ft-lb/in2	ISO 179
	5.50 J/cm2 @Temperature -30.0 °C	26.2 ft-lb/in2 @Temperature -22.0 °F	ISO 179
简支梁缺口冲击强度	1.60 J/cm2	7.61 ft-lb/in2	ISO 179
	1.30 J/cm2 @Temperature -30.0 °C	6.19 ft-lb/in2 @Temperature -22.0 °F	ISO 179

电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电强度	22.0 kV/mm @Thickness 2.00 mm	559 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	350 V @Thickness 3.20 mm	350 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	500 V @Thickness 3.20 mm	500 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
工作温度, Air	115 °C	239 °F	20,000 hr; IEC 216
载荷下热变形温度(0.46 MPa)	262 °C	504 °F	ISO 75, ASTM D648
载荷下热变形温度(1.8 MPa)	257 °C	495 °F	ISO 75, ASTM D648
维卡软化温度	257 °C	495 °F	49 N; ISO 306, ASTM D1525
	260 °C	500 °F	9.8 N; ISO 306, ASTM D1525
可燃性(UL94)	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
极限氧指数	27 %	27 %	ASTM D2863
灼热丝易燃指数	650 °C @Thickness 3.20 mm	1200 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	650 °C @Thickness 0.800 mm	1200 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12

加工性能	额定值 (公制)	额定值 (英制)	测试方法
射嘴温度	285 - 300 °C	545 - 572 °F
1区	270 - 290 °C	518 - 554 °F	hopper
2区	275 - 290 °C	527 - 554 °F
3区	285 - 300 °C	545 - 572 °F
4区	285 - 300 °C	545 - 572 °F
加工（熔体）温度	280 - 300 °C	536 - 572 °F	Do not melt above 300°C
模具温度	100 - 120 °C	212 - 248 °F	Preferred
干燥温度	80.0 - 85.0 °C	176 - 185 °F
干燥时间	4 hour	4 hour
注射压力	70.0 - 100 MPa	10200 - 14500 psi

材料描述		测试方法
Clamping Force	in tons, 0.7 times the projected surface area in cm2
Flammability Rating	B28	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 Mpa